Technical Data:
• Hardness: 56HRC to 62HRC
• Alloying elements: Eutectic tough carbides
• Carbides dispersed: 50 to 60 % at surface
Sizes Available: 6+6;8+8;10+10;12+11;12+18
CASTOFUSE wear plate.
• Very smooth Surface, very low residual stress. (No weld
bead on surface)
• Unique manufacturing process produces a flat fusion line.
• Low friction coefficient properties (Anti Hang up)
• Single pass alloy deposition, Consistent & dense alloy composite microstructure.
• Minimal metal dilution, No plate distortion.
• 100% metallurgical bonding between alloy and base material.
• Controlled colling provides perfect carbide formation.
• Can fabricate &, supply as per drawing prepared parts.
CDP Wear Plate
Extreme hardness without sacrificing formability by
rolling or bending.
Greatly increased service life due to excellent homogeneity and the specific metallurgical characteristics of the
weld deposit.
Ease of welding during installation due to ductile base
metal.
Straightforward cutting by plasma cutting techniques.
Eliminates distortion caused by conventional welding
techniques.
Easily formed and fabricated for custom component manufacturing.
A wide range of custom products for every industrial
application.
Dimensions: 1500X3000 mm (1220X2740 mm Coated 3.34mm2
Type of wearfacing : Chromium Carbide Rich alloy
Hardness: 57-62 HRC
Carbide Content :->30%
Maximum operating temperature: 350 Degree Celsius.
Applications
On road tipper and dumper bodies
Cement drum mixer barrels,
Refuse haulers, scrap containers
Buckets, knives
Feeders, skips, screw conveyors
Mining and earthmoving machinery
Screeners & Chutes
Crushing and pulverizing equipment
Conveyors belts Skirt
Grapples
Scrap presses
EQT 400 -380-410HBW
EQT 450 -420-480HBW
EQT 500 – 470-530HBW
Standard size available: 6000X2000mm,3000X2000mm
EQT
of 400/450/500 HBW. The steel offers very high resistance to abrasive wear and impact
granting a longer service life. The combination of very good cold forming properties
and excellent weldability makes EQT 400 an optimal choice for most wear applications.
EQT 400 is mainly recommended for the following applications:
CastoChrome® Ultimate
• Made-to-order ultimate grade CastoChrome®
• Best-in-mance for engineered parts.
• Proprietary process of tungsten carbide (WC) brazing
• Hardness; HV1500 (HRA90)
CastoChrome® Tuff
Excellent choice for high impact and severe abrasion
Laminated CrMo impact alloy with ceramic inserts
Weldable parts
CastoChrome® Ceram
Proprietary ceramic composite solution for all applications, including ball mill feeder liners, loaf liners, hammers, blow and wear
Chrome casting (Choky Bars or Casting or Wear Liners)
Casto Chrome® Grades
Our Casto Chrome line is available in various grades to combat your unique wear challenges, from
high chromium to tungsten carbides or ceramic infused in chrome-white iron. Contact our wear experts to discuss the best solution for your application.
Casto Chrome® 700+
• Go-to grade for all standard HCWI parts
• CrMo alloy containing primary carbides
• Nominal hardness of 700+ BHN (HRC63+)
CastoChrome® Plus
• Made-to-order superior alloy-enriched grade
• Enhanced performance
• Proprietary process tungsten carbide (WC) fusion
• Hardness; HV950 (HRA85)
Applications:
Mines and quarries
Cement and ready-mix concrete plants
Sand and gravel pits
Brickworks
Shredders and recycling plants
Foundries and coking plants
Iron and steel mills
Incineration plants and electric power stations
Hardness: 55 to 60 HRC
Casto Tube
Preventive protection against severe abrasion and erosion
Small diameter, seamless CastoTubes for
superior industrial performance:
Extremely wear resistant, lightweight
and easy-to-join
Highly cost effective for rapid replacement of worn tubes
Increase service life, plant availability
and process productivity
Casto Slurry (Slurry Hoses)
. straight piece RUBBER-CERAMIC
composite hoses
CastoSLURRY offers a range of versatile mining hoses, including T-pieces, elbows, straight pipes, and hoses, with ceramic-lined options suitable for
demanding suction and discharge tasks. These top-quality products are crafted in Ireland and the UAE, providing the ideal solution for applications involving severe wear and the need for flexibility.